Test item |
Unit |
SampleCategory |
Results |
Test method |
Loss ignition |
% |
– |
29.6 |
ASTM D2584-11 |
Specific Gravity((23/23)℃) |
– |
– |
1.88 |
ASTM D792-13(A Method)) |
Tensile strength |
MPa |
– |
111 |
ASTM D638-14(*) |
Flexural strength |
MPa |
– |
208 |
ASTM D790-17(**) |
Flexural modulus of elasticity |
GPa |
– |
10.5 |
ASTM D790-17(**) |
Izod Impact Strength |
J/m |
– |
1.203(P) |
ASTM D256-10e1(A Method) |
Izod Impact Strength(~40℃) |
J/m |
– |
1.484(P) |
ASTM D256-10e1(A Method)(***) |
Load deformation temperature(1.82MPa) |
℃ |
– |
measurable(****) |
ASTM D648-16(B Method)) |
Absorption rate(24h Immersion) |
% |
– |
0.47 |
ASTM D570-98(2010)e1 |
* Test speed : 5 mm/min, Test surface : Type I / ** Test speed : 1.4 mm/min, Distance Between Supports : 50 mm / *** Status control : (-40 ±2) ℃ X 30 min / **** Specified deformation (0.25 mm) does not occur up to maximum temperature of equipment (300 ° C)